310 Stainless steel Seamless tubes

 
Principal Design Features  The strength of this alloy is a combination of good strength and corrosion resistance in temperatures up to 2100 F (1149 C). Due to its relatively high chromium and nickel content it is superior in most environments to 304 or 309 stainless. 

Applications  Oven linings, boiler baffles, kilns, lead pots, radiant tubes, annealing covers, saggers, burners, combustion tubes, refractory anchor bolts, fire box sheets, furnace components and other high temperature containers. 

Machinability  This alloy machines similarly to type 304 stainless. Its chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers. 

Welding  Most of the austenitic stainless steels can be readily welded using fusion or resistance methods. Oxyacetylene welding is not recommended. Filler metal should be AWS E/ER 310. 

Hot Working  Most common hot work methods can be successfully performed after uniform heating to 2150 F (1177 C). Do not forge below 1800 F (982 C). Rapid cooling is required to maximize corrosion resistance. 

Cold Working  Although this alloy has a high work hardening rate, it can be drawn, headed, upset, and stamped. Full annealing is required after cold work to remove internal stress. 

Annealing  1900-2050 F (1038-1121 C) water quench. 

310S Stainless steel Seamless tubes

Principal Design Features  The strength of this alloy is a combination of good strength and corrosion resistance in temperatures up to 2100 F (1149 C). Due to its relatively high chromium and nickel content it is superior in most environments to 304 or 309 stainless. 

Applications  Oven linings, boiler baffles, fire box sheets, furnace components and other high temperature containers. 

Machinability  This alloy machines similarly to type 304 stainless. Its chips are stringy and it will work harden rapidly. It is necessary to keep the tool cutting at all times and use chip breakers. 

Welding  Most of the austenitic stainless steels can be readily welded using fusion or resistance methods. Oxyacetylene welding is not recommended. Filler metal should be AWS E/ER 310. 

Hot Working  Most common hot work methods can be successfully performed after uniform heating to 2150 F (1177 C). Do not forge below 1800 F (982 C). Rapid cooling is required to maximize corrosion resistance. 

Cold Working  Although this alloy has a high work hardening rate, it can be drawn, headed, upset, and stamped. Full annealing is required after cold work to remove internal stress. 

Annealing  1900-2050 F (1038-1121 C) water quench. 

Hardening  This alloy does not respond to heat treatment. Cold work will cause an increase in both hardness and strength.